"Test Method:","MTS Tensile PVC.msm"

"Sample","Spcmn","Width","Thickness","Break Load","Area","Break Stress","Elongation At Break","%Strain At Peak"
"I. D.","No.","mm","mm","N","mm^2","MPa","mm","%"

"Sample1.mss","1","12.700","3.175","85.988","40.3225","2.132","128.546","253.044"
"Sample1.mss","2","12.700","3.175","****","40.3225","****","****","34.437"
"Sample1.mss","3","12.700","3.175","26.645","40.3225","0.661","46.479","84.277"
"Sample1.mss","4","12.700","3.175","65.232","40.3225","1.618","68.979","135.786"
"Sample1.mss","5","12.700","3.175","11.714","40.3225","0.290","62.032","43.370"
"Sample1.mss","6","12.700","3.175","58.334","40.3225","1.447","48.381","95.238"
"Sample1.mss","7","12.700","3.175","0.587","40.3225","0.014","20.579","25.419"
"Sample1.mss","8","12.700","3.175","21.746","40.3225","0.539","11.664","22.631"
"Sample1.mss","9","12.700","3.175","****","40.3225","****","****","18.845"
"Sample1.mss","10","12.700","3.175","58.527","40.3225","1.451","67.701","133.270"
"Sample1.mss","11","12.700","3.175","1.293","40.3225","0.032","129.579","26.402"
"Sample1.mss","12","12.700","3.175","24.394","40.3225","0.605","108.452","110.469"
"Sample1.mss","13","12.700","3.175","40.524","40.3225","1.005","0.282","0.556"
"Sample1.mss","14","12.700","3.175","5.041","40.3225","0.125","142.689","100.439"
"Sample1.mss","15","12.700","3.175","****","40.3225","****","****","31.056"
"Sample1.mss","16","12.700","3.175","85.343","40.3225","2.116","54.226","105.595"
"Sample1.mss","17","12.700","3.175","0.082","40.3225","0.002","0.000","0.000"
"Sample1.mss","18","12.700","3.175","28.962","40.3225","0.718","34.708","55.036"
"Sample1.mss","19","12.700","3.175","****","40.3225","****","****","31.993"